Its aqueous solution is of surface activity, high transparency and stability, when heated to certain temperature, the solution becomes cloudy and gelling quickly, however, the solution become clear again after cooling.
HPMC has different types varying from its gelling temperature. The solubility is differed from its viscosity, the lower the viscosity, the higher the solubility. However, the solubility in water is not subject to pH value of its aqueous solution.
The lower methoxyl content of HPMC, the higher gelling temperature, the lower solubility and surface activity.

Dissloving method:
-Heat the water to above 85 and slowly add HPMC under slow agitation to gradually form uniform pulp, then cool the solution under agitation until it become transparent.
-Heat certain quantity of water (normally one third or two third) to above 85 , slowly add HPMC under slow agitation to gradually form uniform pulp, then add cooling water into solution, stir and cool the solution at about 20℃ to be clear.
-Mix HPMC and other powder materials together, then add water and stir.
-Add HPMC into ethanol or other solvents to be dispersed, then add water and stir.

Specifications:
Appearance: White to off-white powder
Gelling temperature, deg C:70-90
Methoxyl content, %: 19.0-24.0
Hydroxypropyl content, %: 4.0-12.0
Viscosity, mpa.s@ 20 deg C,2%: 10-200000
Loss on drying, %: 5.0 max.
Ash, %: 1.0 max.
pH: 4-8

Applications:
HPMC is widely used as thickener, binder, surfactant, lubricant, suspension aid, stabilizer, emulsifier, excipient, water retention agent, film-forming agent in PVC processing, construction, coating and paints, food, pharmaceuticals, cosmetics etc.

Packing: 25kg bag
Storage: Store in cool, dry and ventilated place, keep away from sunlight, rain, and dampness.